Usporedba mikrostrukture i mehaničkih svojstava ekstrudiranih aluminijevih legura iz serije 6000

završni rad

• Naslov (engleski): Comparison microstructure and mechanical properties of extruded 6000 series aluminium alloys
• Autor: Iva Ćavar
• Mentor: Vera Rede (mentor)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet strojarstva i brodogradnje; Zagreb
• Datum i država obrane: 2022-03-02, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Strojarstvo

Sažetak

U završnom radu provedena je usporedba mikrostrukture i mehaničkih svojstava četiriju ekstrudiranih aluminijevih legura s magnezijem i silicijem, iz serije 6000. Navedene legure imaju vrlo sličan kemijski sastav, a pojedinačni maseni udjeli magnezija i silicija su ispod 1%.
Mikrostrukture svih legura sastoje se uglavnom od kristala mješanaca te sitnih homogeno raspoređenih precipitata intermetalne faze Mg2Si. Legure koje su sporije hlađene imaju viši volumni udio i homogeniji raspored precipitata.
Vrijednosti mikrotvrdoće analiziranih legura su u rasponu od 60 HV0,2 do 76 HV0,2, a više vrijednosti izmjerene su kod sporije hlađenih legura. Vrijednosti makrotvrdoće kreću se od 73 HB do 95 HB, a više vrijednosti izmjerene su kod brže hlađenih legura.
Više vrijednosti granice razvlačenja i više vrijednosti vlačne čvrstoće te niže vrijednosti istezljivosti izmjerene su kod legura koje su brže hlađene. Vrijednosti granice razvlačenja su u rasponu od 192 do 245 N/mm2, vrijednosti vlačne čvrstoće su od 214 do 260 N/mm2, a istezljivosti od 5,4 do 7,6 %.
Rasipanja rezultata svih provedenih ispitivanja su vrlo mala.

Sažetak (engleski)

This project compares the microstructure and mechanical properties of four extruded aluminium alloys with magnesium and silicon, from the 6000 series. These alloys have similar chemical compositions and the individual mass fractions of magnesium and silicon are less than 1%.
The microstructure of all alloys consists mainly of mongrel crystals and small homogeneously distributed precipitates of the intermetallic phase Mg2Si. Slower cooled alloys show a higher volume fraction and a more homogeneous distribution of precipitates.
The microhardness of the alloys investigated ranged from 60 HV0.2 to 76 HV0.2 with higher values measured for slower-cooled alloys. The values for macro hardness ranged from 73 HB to 95 HB, with higher values measured for faster cooled alloys.
Higher values of yield strength and higher values of tensile strength and lower values of elongation were measured for alloys that were cooled faster. Yield strength values ranged from 192 to 245 N/mm2, tensile strength values ranged from 214 to 260 N/mm2 and elongation values ranged from 5.4 to 7.6 %.
The discrepancies between the results of all the tests carried out are very small.

• Ključne riječi: aluminijeve legure; ekstruzija; mikrostruktura; mehanička svojstva
• Ključne riječi (engleski): aluminium alloys; extrusion; microstructure; mechanical properties
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:235:627427
• Studijski program: Naziv: Strojarstvo; Vrsta studija: sveučilišni; Stupanj studija: preddiplomski; Akademski / stručni naziv: sveučilišni/a prvostupnik/ prvostupnica (baccalaureus/baccalaurea) inženjer/inženjerka strojarstva (univ. bacc. ing. mech.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2022-02-25 09:21:24