Utjecaj aditivne proizvodnje električnim lukom i žicom na mikrostrukturu dupleks čelika

diplomski rad

• Naslov (engleski): Influence of wire and arc additive manufacturing on microstructure of duplex steel
• Autor: Stipe Ljušanin
• Mentor: Ivica Garašić (mentor)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet strojarstva i brodogradnje; Zagreb
• Datum i država obrane: 2021-12-16, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Strojarstvo; Proizvodno strojarstvo

Sažetak

U teorijskom dijelu rada opisana je aditivna proizvodnja te aditivna proizvodnja električnim lukom i žicom. Opisani su razvoj i svojstva dupleks čelika te je objašnjen utjecaj toplinske obrade i pojedinih legirnih elemenata na mikrostrukturu i zavarljivost dupleks čelika. Detaljno je opisan MAG postupak zavarivanja s posebnim naglaskom na načinu prijenosa metala.
U eksperimentalnom dijelu rada na temelju prethodno izrađenog zida coldArc postupkom osmišljen je plan izrade uzoraka za ispitivanje. Kao dodatni materijal koristio se dupleks čelik. Za svako ispitivanje opisan je postupak i korištena oprema. Jedan dio uzoraka podvrgnut je toplinskoj obradi kako bi se pokazao utjecaj toplinske obrade na mikrostrukturu i svojstva zida. Analizom dobivenih rezultata utvrđen je utjecaj na svojstva i mikrostrukturu zida izrađenog coldArc postupkom.

Sažetak (engleski)

The theoretical part of the thesis describes additive manufacturing and wire and arc additive manufacturing. The development and properties of duplex steels are described, and the influence of heat treatment and individual alloying elements on the microstructure and weldability of duplex steels is explained. The MAG welding process is described in detail with special emphasis on the method of metal transfer.
In the experimental part of the thesis, based on the previously made wall by the coldArc modified procedure, a plan for making samples for testing was devised. Duplex steel was used as an additional material. For each test, the procedure and equipment used are described. One part of the samples was exposed to heat treatment to show the influence of heat treatment on the microstructure and properties of wall. The analysis of the obtained results determined the influence on the properties and microstructure of the wall made by the coldArc method.

• Ključne riječi: WAAM; coldArc; dupleks čelik; mikrostruktura
• Ključne riječi (engleski): WAAM; coldArc; duplex steel; microstructure
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:235:228287
• Studijski program: Naziv: Strojarstvo; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka strojarstva (mag. ing. mech.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2021-12-01 21:08:42