Optimiranje parametara zavarivanja pri aditivnoj proizvodnji električnim lukom i žicom

završni rad

• Naslov (engleski): Optimisation of welding parameters for wire arc additive manufacturing
• Autor: Jurica Vresk
• Mentor: Ivica Garašić (mentor)
• Član povjerenstva: Vinko Šimunović (predsjednik povjerenstva)
• Član povjerenstva: Zdenka Keran (član povjerenstva)
• Član povjerenstva: Zoran Kožuh (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet strojarstva i brodogradnje; Zagreb
• Datum i država obrane: 2020-02-28, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Strojarstvo; Proizvodno strojarstvo

Sažetak

U završnom radu obrađena je tema aditivne proizvodnje žicom i električnim lukom (engl.
Wire and Arch Additive Manufacturing – WAAM) konstrukcijskog čelika S355. Rad se sastoji od
teorijskog i eksperimentalnog dijela.
U teorijskom dijelu rada objašnjeni su osnovne aditivne proizvodnje i temeljni princip
postupka aditivne proizvodnje žicom i električnim lukom (WAAM). Teorijski je obrađeno
korištenje čelika S355 u navedenoj tehnologiji. Konstrukcijski čelici opisani su iz razloga što je
jedan od njih (S355) korišten u samoj izvedbi eksperimentalnog dijela. Opisan je MAG postupak
zavarivanja, njegove osnove, princip rada, a detaljno su obrađeni i primjeri primjene ovog
postupka zavarivanja za aditivnu proizvodnju žicom i električnim lukom.
U eksperimentalnom dijelu rada određeni su optimalni parametri za aditivnu proizvodnju
električnim lukom i žicom konstrukcijskog čelika S355 iz kojeg je primjenom robotiziranog
zavarivanja izrađena tri uzorka. Uzorci se razlikuju ovisno o parametrima koji su bili korišteni
robotiziranim MAG postupkom zavarivanja. Na izrađenim uzorcima je izmjerena tvrdoća po
Vikersu (HV10). Također, u radu je izvršeno 3D skeniranje izrađenih zidova (uzoraka) te su
određeni parametri teksture površine. Izvršena je mehanička obrada glodanjem da bi se osim
simulacijski, BTF omjer mogao odrediti i praktično, vaganjem prije te nakon obrade.

Sažetak (engleski)

In this thesis, the topic of Wire and Arch Additive Manufacturing-WAAM construction steels
is discussd. The paper consists of a theoretical and experimental part.
Theoretical part explains the basic principles of Additive Manufacturing and the basic
principle of Wire and Arch Additive Manufacturing (WAAM). Also theoretical part explains using
of construction steel S355 in this technology. Construction steels are described because one of the
steels is used in experiment. The MAG welding process, its basis, the principle of operation, and
the examples of the application of this welding procedure for Wire and Arch Additive
Manufacturing are described.
In the experimental part of the work, optimal parameters for Wire and Arch Additive
Manufacturing of construction steel S355 was obtained, from which three samples were made
using robotized welding. Differences between the sampels are in parametars which were used in
robotized MAG welding. Hardness was measured by Vickers hardness test (HV10). Also, 3D
scanning of created walls (samples) has been performed and surface texture parameters were
determined. Milling was performed on both sides of sample to the white color because sample was
used in mesuring weight of samples to describe BTF ratio.

• Ključne riječi: Aditivna proizvodnja žicom i električnim lukom; konstrukcijski čelik S355; MAG postupak zavarivanja
• Ključne riječi (engleski): Wire and arch additive manufacturing; construction steel S355; MAG welding process
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:235:818463
• Studijski program: Naziv: Strojarstvo; Vrsta studija: sveučilišni; Stupanj studija: preddiplomski; Akademski / stručni naziv: sveučilišni/a prvostupnik/ prvostupnica (baccalaureus/baccalaurea) inženjer/inženjerka strojarstva (univ. bacc. ing. mech.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2020-02-28 12:22:19