Utjecaj zaštitnog plina pri TIG zavarivanju titana

diplomski rad

• Naslov (engleski): Influence of shielding gas at TIG welding of titanium
• Autor: Matija Vukoja
• Mentor: Ivica Garašić (mentor)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet strojarstva i brodogradnje; Zagreb
• Datum i država obrane: 2018-12-06, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Strojarstvo

Sažetak

Cilj ovog diplomskog rada je odrediti utjecaj brzine zavarivanja i mješavine zaštitnog plina kod TIG zavarivanja titanija na dubinu penetracije. U teorijskom dijelu rada iznesene su karakteristike titanija i njegovih legura kao karakteristike pojedinih postupaka kojima se uobičajeno zavaruje navedeni materijal. Detaljnije je analiziran TIG postupak te detalji vezani uz njega kao korišteni dodatni materijal, plinske mješavine, specifičnosti pri zavarivanju titanija ovim postupkom te uobičajeni parametri rada. U eksperimentalnom dijelu rada u laboratoriju su rađeni navari mehaniziranim TIG postupkom na uzorcima titanija pri čemu su korištene dvije mješavine zaštitnog plina te dvije različite brzine zavarivanja kako bi se utvrdio njihov utjecaj na dubinu penetracije. Nakon izvedenog navarivanja analizirana je profil zavara te je izmjerena dubina penetracije. Na osnovu izmjerenih vrijednosti doneseni su zaključci o utjecaju mješavine zaštitnog plina kao i brzine zavarivanja na dubinu penetracije za TIG postupak zavarivanja titanija.

Sažetak (engleski)

The aim of this master's thesis is to determine the influence of welding speed and shielding gas mixture on the depth of penetration for TIG welding of titanium. The characteristics of titanium and it's alloys along with the characteristics of welding procedures usually used for joining them are examined in the theoretical part. The TIG process is further analyzed along with the details regarding filler materials, gas mixtures and specificities are examined regarding welding titanium with this procedures along with the typical welding parameters. The experimental research was done in the laboratory and it included a mechanized TIG process used to make beads while two different shielding gas mixtures and welding speeds were used to determine their influence on the depth of penetration. After the welding procedure was done, the weld profile was analyzed and the depth of penetration was measured. Based on the measurements obtained conclusions were made on the influence of the shielding gas and welding speed on the depth of penetration for TIG welding of titanium.

• Ključne riječi: TIG zavarivanje; titanij; dubina penetracije; zaštitni plin; brzina zavarivanja
• Ključne riječi (engleski): TIG procedure; titanium; depth of penetration; shielding gas; welding speed
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:235:298612
• Studijski program: Naziv: Strojarstvo; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka strojarstva (mag. ing. mech.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2019-05-22 23:33:10