diplomski rad

• Naslov (engleski): Advanced industrial coatings
• Autor: Ante Milić
• Mentor: Vinko Šimunović (mentor)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet strojarstva i brodogradnje; Zagreb
• Datum i država obrane: 2019-03-21, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Strojarstvo

Sažetak

Diplomski rad sastoji se od teorijskog i eksperimentalnog dijela. U teorijskom dijelu rada prikazan je pregled literature značaja zaštite od korozije, troškova uzrokovanih korozijom te mehanizama zaštite od korozije. Detaljnije je obrađena zaštita od korozije organskim premazima, mehanizmi sušenja premaza te sušenje premaza infracrvenim (IC) zračenjem. Na kraju, obrađena je teoretska podloga elektrokemijske impedancijske spektroskopije (EIS). U eksperimentalnom dijelu rada opisana je provedba procesa pripreme, nanošenja te sušenja premaza, kao i ispitivanja čistoće površine, ispitivanja hrapavosti površine, ispitivanja debljine suhog filma premaza, ispitivanja otpornosti prema koroziji u slanoj i vlažnoj komori, određivanje vremena sušenja premaza, ispitivanje prionjivosti premaza, ispitivanje sjaja premaza te ispitivanje otpora premaza elektrokemijskom impedancijskom spektroskopijom, zaključno s određivanjem poroznosti premaza metalografskom metodom. Cilj ispitivanja bio je utvrditi razlike u fizikalnim i kemijskim svojstvima premaza sušenim na sobnoj temperaturi i premazima sušenim infracrvenim (IC) emiterom na različitim udaljenostima od istog.

Sažetak (engleski)

This graduate thesis consists of two parts: theoretical and experimental. The theoretical part of the thesis presents a literature review on the importance of corrosion protection, corrosion related costs and corrosion protection mechanisms. The protection against corrosion with organic coatings, coating drying mechanisms and the drying of coating with infrared (IR) radiation are discussed in more detail. Finally, the theoretical background of electrochemical impedance spectroscopy (EIS) is elaborated. In the experimental part of the thesis, the process of preparation, application and the drying of coatings are described along with several tests which were carried out: cleanliness of uncoated steel substrates test, surface roughness test, dry film thickness test, corrosion tests in salt spray and humid chamber, drying time determination, pull-off adhesion test, determination of gloss value of coatings, coating resistance test by electrochemical impedance spoectroscopy and determination of the porosity of the coating by means of metallographic method. The aim of the study was to determine the differences between the physical and chemical properties of the coatings dried at atmospheric conditions, and the coatings dried by the infra-red (IR) emitter at different distances from the same.

• Ključne riječi: korozija; zaštita od korozije; organski premazi; infracrveno (IC) sušenje premaza; elektrokemijska impedancijska spektroskopija (EIS)
• Ključne riječi (engleski): corrosion; corrosion protection; organic coatings; infrared (IR) curing of coatings; electrochemical impedance spectroscopy (EIS)
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:235:188911
• Studijski program: Naziv: Strojarstvo; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka strojarstva (mag. ing. mech.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup; Datum isteka embarga: 2021-3-20
• Datum i vrijeme pohrane: 2019-05-23 00:41:44