Toplinska obrada zavara od aluminijeve legure EN-AW 6082

diplomski rad

• Naslov (engleski): Heat treatment of aluminum alloy EN-AW 6082 welds
• Autor: David Islam
• Mentor: Darko Landek (mentor)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet strojarstva i brodogradnje; Zagreb
• Datum i država obrane: 2024-11-05, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Strojarstvo

Sažetak

Aluminijske legure imaju široku primjenu u industriji zbog svojeg omjera mase i čvrstoće i otpornosti na koroziju. Njihova svojstva moguće je dodatno unaprijediti precipitacijskim očvršćivanjem, temperaturno-vremenskim procesom kojim se povećava čvrstoća materijala. Zavarivanje ovih legura zahtijeva preciznu kontrolu kako bi se izbjegli problemi poput poroznosti i promjena u zoni zahvaćenoj toplinom, a postupci poput AC i DC MIG-a najčešće se koriste za njihovo spajanje.
U teorijskom dijelu opisane su precipitacijski očvrstive aluminijske legure, koje su sistematizirane i klasificirane unutar skupine aluminijskih legura. Poseban naglasak je stavljen na njihov kemijski sastav, svojstva, karakteristike i pripadnost određenim skupinama aluminijevih legura. Detaljno su opisani procesi i mehanizmi precipitacijskog očvršćivanja uz poseban fokus na parametre koji uvjetuju te procese. Analizirani su i najčešći postupci zavarivanja aluminijskih legura, poput MIG-a uz razmatranje glavnih izazova povezanih s tim metodama, kao što su nastanak pukotina, osobine zone utjecaja topline (ZUT) i pojava poroznosti u zavarenim spojevima.
U eksperimentalnom dijelu rada provest će se žarenje uzoraka osnovnog materijala, žarenje zavarenih uzoraka i analiza mikrostrukture žarenih uzoraka zavara. Žarenje uzoraka osnovnog materijala provest će se zbog određivanja parametara žarenja zavarenih uzoraka s ciljem minimiziranja sniženja tvrdoće. Mikrostruktura zavara je analizirana radi usporedbe grešaka zavarivanja i traženja promjena u mikrostrukturi uzrokovanih zavarivanjem i žarenjem.

Sažetak (engleski)

Aluminum alloys are widely used in industry due to their strength-to-weight ratio and corrosion resistance. Their properties can be further enhanced through precipitation hardening, a temperature-time process that increases material strength. Welding these alloys requires precise control to avoid issues such as porosity and changes in the heat-affected zone (HAZ), with methods like AC and DC MIG welding being the most commonly used for joining.
The theoretical section describes precipitation-hardened aluminum alloys, which are systematized and classified within the group of aluminum alloys. Particular emphasis is placed on their chemical composition, properties, characteristics, and classification into specific aluminum alloy groups. The processes and mechanisms of precipitation hardening are thoroughly explained, with a special focus on the parameters that influence these processes. Additionally, common welding methods for aluminum alloys, such as MIG welding, are analyzed, addressing the main challenges associated with these techniques, including crack formation, the characteristics of the heat-affected zone (HAZ), and the occurrence of porosity in welded joints.
In the experimental section, annealing of base material samples, annealing of welded samples, and analysis of the microstructure of annealed weld samples will be conducted. Annealing of the base material samples will be performed to determine the annealing parameters for welded samples, with the goal of minimizing hardness reduction. The microstructure of the welds will be analyzed to compare welding defects and identify changes in the microstructure caused by welding and annealing.

• Ključne riječi: aluminijske legure; precipitacijsko očvršćivanje; zavarivanje; MIG; žarenje
• Ključne riječi (engleski): aluminum alloys; precipitation hardening; welding; MIG; annealing
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:235:232092
• Studijski program: Naziv: Strojarstvo; smjerovi: Konstrukcijski smjer, Procesno-energetski smjer, Proizvodni smjer, Inženjersko modeliranje i računalne simulacije, Brodostrojarski smjer, Industrijsko inženjerstvo i menadžment, Inženjerstvo materijala, Mehanika i robotika, Autonomni sustavi i računalna inteligencija, Mehatronika i robotika; Smjer: Inženjerstvo materijala; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: sveučilišni/a magistar/magistra inženjer/inženjerka strojarstva (univ. mag. ing. mech.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2024-11-27 11:19:31