Određivanje vibracija i zagrijavanja nitriranog igličastog ležaja

završni rad

• Naslov (engleski): Determination of vibration and heating of nitrided needle bearing
• Autor: Ivan Brkić
• Mentor: Darko Landek (mentor)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet strojarstva i brodogradnje; Zagreb
• Datum i država obrane: 2024-09-26, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Strojarstvo; Opće strojarstvo (konstrukcije)

Sažetak

U teorijskom dijelu rada opisani su igličasti ležaji, njihove karakteristike, postupci nitriranja
prstena ležaja te metode ispitivanja hrapavosti površine, mjerenje temperature i vibracija
ležaja. U eksperimentalnom dijelu provedeno je nitriranje unutarnjeg prstena igličastog ležaja
od čelika 100Cr6 u plazmi N2+H2 i nitrokarburiranje u solnoj kupci TENIFER. Provedeno je
ispitivanje hrapavosti površina nenitriranog i nitriranih prstenova koje je pokazalo povećanje
hrapavosti primjenom nitrokarburiranaj u solnoj kupci, dok nitriranje u plazmi nije značajnije
utjecalo na hrapavost površine. Nenitrirani i nitrirani prstenovi izloženi su vrtnji u igličastom
ležaju bez opterećenja, pri brzinama 950 min-1, 1025 min-1 i 1215 min-1 u trajanju od 1 min,
bez podmazivanja. Tijekom rotacije igličastih ležaja provedena su mjerenja vibracija, buke i
temperaturnog polja ležaja. Iz provedenih ispitivanja, može se zaključiti da unutarnji prsteni
nitrirani u plazmi te prsteni nitrokarburirani postupkom TENIFER, imaju bolja svojstva nego
prsten u polaznom stanju, odnosno manje se zagrijavaju, imaju manji nivo buke i amplitudu
vibracija.

Sažetak (engleski)

In the theoretical part of the work, needle bearings, their characteristics, nitriding procedures of
the bearing rings and methods of testing the surface roughness, measuring the temperature and
vibration of the bearing are described. In the experimental part, nitriding of the inner ring of the
needle bearing made of 100Cr6 steel in N2+H2 plasma and nitrocarburizing in the TENIFER
salt bath were carried out. The surface roughness of non-nitrided and nitrided rings was tested,
which showed an increase in roughness with the use of nitrocarburized in salt water, while
nitriding in plasma did not significantly affect the surface roughness. Non-nitrided and nitrided
rings are exposed to rotation in a needle bearing without load, at speeds of 950 min-1, 1025
min-1 and 1215 min-1 for 1 min, without lubrication. During the rotation of the needle bearings,
measurements of vibrations, noise and the temperature field of the bearing were carried out.
From the conducted tests, it can be concluded that inner rings nitrided in plasma and rings
nitrocarburized by the TENIFER process have better properties than the ring in its initial state,
i.e. they heat up less, have a lower noise level and vibration amplitude.

• Ključne riječi: Ključne riječi: igličasti ležaj; 100Cr6; prsten; nitriranje; površina; TENIFER; temperatura; vibracije.
• Ključne riječi (engleski): needle bearing; 100Cr6; ring; nitriding; surface; TENIFER; temperature; vibrations
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:235:673922
• Studijski program: Naziv: Strojarstvo; Vrsta studija: sveučilišni; Stupanj studija: prijediplomski; Akademski / stručni naziv: sveučilišni/a prvostupnik/prvostupnica (baccalaureus/baccalaurea) inženjer/inženjerka strojarstva (univ. bacc. ing. mech.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2024-09-25 21:15:08