Analiza mehanizma nastanka i redukcije deformacija pri MIG zavarivanju aluminijskih legura

diplomski rad

• Naslov (engleski): Analysis of formation mechanism and reduction of distortions in MIG welding of aluminium alloys
• Autor: Šime Lovrić
• Mentor: Ivica Garašić (mentor)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet strojarstva i brodogradnje; Zagreb
• Datum i država obrane: 2024-07-15, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Strojarstvo; Proizvodno strojarstvo

Sažetak

Cilj ovog diplomskog rada je analizirati mehanizme nastanka i redukcije deformacija pri MIG zavarivanju aluminijskih legura. U teorijskom dijelu rada opisani su postupci zavarivanja aluminijskih konstrukcija u brodogradnji s posebnim osvrtom na MIG postupak zavarivanja. Detaljno je objašnjena klasifikacija aluminijskih legura, definirani su i pojašnjeni pojmovi zaostalih naprezanja i deformacija. Također, u teorijskom dijelu rada navedene su i metode kojima je moguće smanjiti zaostala naprezanja i deformacije.
U eksperimentalnom dijelu rada razrađena je tehnologija zavarivanja I profila DC MIG-P i AC MIG-P postupkom te je provedeno zavarivanje četiri ispitna uzorka. Izrađena je naprava za stezanje I profila prilikom zavarivanja te je provedena analiza deformacija pri zavarivanju s i bez primjene naprave. Na temelju dobivenih rezultata eksperimentalnog rada donesen je zaključak.

Sažetak (engleski)

The objective of this thesis is to analyze the mechanisms of occurrence and reduction of deformations in MIG welding of aluminum alloys. The theoretical part of the thesis describes the welding processes of aluminum structures in shipbuilding, with a special focus on the MIG welding process. The classification of aluminum alloys is explained in detail, and the concepts of residual stresses and deformations are defined and clarified. Additionally, the theoretical part outlines methods that can be used to reduce residual stresses and deformations.
In the experimental part of the thesis, the welding technology of I profiles using the MIG-P and AC MIG-P processes was elaborated, and welding of four test samples was carried out. A clamping device for I profiles during welding was created, and an analysis of deformations during welding with and without the use of the device was conducted. Based on the results obtained from the experimental work, a conclusion was drawn.

• Ključne riječi: aluminij; zaostala naprezanja; deformacije; zavarivanje MIG postupkom
• Ključne riječi (engleski): aluminum; residual stresses; deformations; MIG welding
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:235:934623
• Studijski program: Naziv: Strojarstvo; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka strojarstva (mag. ing. mech.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2024-07-11 16:24:21