Žarenje za smanjenje zaostalih naprezanja u zavarima čelika S235JR

diplomski rad

• Naslov (engleski): Stress-relief annealing in S235JR steel welds
• Autor: Kristian Zorić
• Mentor: Darko Landek (mentor)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet strojarstva i brodogradnje; Zagreb
• Datum i država obrane: 2023-01-26, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Strojarstvo; Opće strojarstvo (konstrukcije)

Sažetak

U radu je opisano elektrolučno zavarivanje pod praškom (EPP) dvije ploče od čelika S235 debljine 120 mm. U teorijskom dijelu rada opisana su svojstva i primjena konstrukcijskog čelika S235, postupak zavarivanja pod praškom, nastanak zaostalih naprezanja u zavaru, te postupci toplinske obrade žarenja za smanjenje zaostalih naprezanja. U eksperimentalnom dijelu rada provođena su žarenja za redukciju zaostalih naprezanja s različitim parametrima žarenja u manjoj i većoj električnoj peći. Utjecaj žarenja praćen je ispitivanjem tvrdoće i mjerenjem zaostalih naprezanja rendgenskom difrakcijom. Provedena su žarenja za smanjenje zaostalih naprezanja u laboratorijskoj električnoj peći i industrijskoj vakuumskoj peći s parametrom žarenja P = 17,16. Žarenja u laboratorijskoj peći nisu popustila zaostala naprezanja zbog nejednoličnog zagrijavanja i ohlađivanja presjeka uzorka. Žarenje uzorka u industrijskoj vakuumskoj peći na 560 °C/4 h smanjila su zaostala naprezanja na cijelom presjeku na vrijednosti između -20 MPa do -50 MPa.

Sažetak (engleski)

This paper describes submerged arc welding (SAW) of two S235 steel plates with a thickness of 120 mm. In the theoretical part of the paper, the properties and application of structural steel S235, the submerged arc welding process, the generation of residual stresses in the weld and the annealing heat treatment procedures to reduce residual stresses are described. In the experimental part of the paper, annealing was performed to reduce residual stresses with different annealing parameters in a smaller and larger electric furnace. The influence of annealing was detected by hardness testing and measurement of residual stresses by X-ray diffraction. Annealings were carried out to reduce residual stresses in a laboratory electric furnace and an industrial vacuum furnace with the annealing parameter P = 17,16. Annealings in the laboratory furnace did not relieve residual stresses due to non-uniform heating and cooling of the sample cross-section. Annealing the sample in an industrial vacuum furnace at 560 °C / 4 h reduced the residual stresses on the entire section to values between -20 MPa and -50 MPa.

• Ključne riječi: zavarivanje pod praškom; čelik S235; žarenje za smanjenje zaostalih naprezanja; zaostala naprezanja u zavaru
• Ključne riječi (engleski): submerged arc welding; steel S235; annealing to reduce residual stresses; residual stresses in the weld
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:235:103840
• Studijski program: Naziv: Strojarstvo; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka strojarstva (mag. ing. mech.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2023-01-18 15:55:29