Utjecaj procesnih parametara sinteriranja na gustoću aluminijeve oksidne keramike

diplomski rad

• Naslov (engleski): Effect of sintering process parameters on density of alumina ceramics
• Autor: Martina Eva Tonković
• Mentor: Lidija Ćurković (mentor)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet strojarstva i brodogradnje; Zagreb
• Datum i država obrane: 2019-01-24, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Strojarstvo

Sažetak

U ovom radu oblikovani su uzorci alumijeve oksidne keramike lijevanjem stabilne suspenzije u gipsani kalup. U tu svrhu pripremljena je 70%-tna vodena suspenzija aluminijevog oksida uz dodatak disperzanta Dolapixa CE-64. Vodena Al2O3 suspenzija homogenizirana je u planetarnom kugličnom mlinu. Sirovci su oblikovani lijevanjem suspenzije u gipsani kalup, te sinterirani u električnoj peći. Ispitan je utjecaj tri različita parametra sinteriranja (temperature sinteriranja, brzine ugrijavanja pri sinteriranju te trajanja držanja na temperaturi sinteriranja) na gustoću sinterirane Al2O3 keramike.
Procjena utjecaja tri parametra sinteriranja (temperature sinteriranja, brzine ugrijavanja pri sinteriranju te trajanja držanja na temperaturi sinteriranja) na gustoću uzoraka aluminijeve oksidne keramike provedena je metodom odzivnih površina (eng. Response surface metodology) na osnovi ekperimentalnih podataka dobivenih prema Box-Behnkenovom planu pokusa, uz primjenu programskog paketa Design-Expert 11.

Sažetak (engleski)

Aluminum oxide ceramic samples were made for this thesis from stable suspension, using slip casting method. 70% aqueous suspension of aluminum oxide was made with the addition of dispersant Dolapix CE-64. Aqueous Al2O3 suspension was then homogenized in planetary ball mill. Samples were molded by slip casting using plaster molds, and sintered in electric furnace. Effect of three different sintering parameters (sintering temperature, sintering heating speed and sintering duration) on density of sintered alumina ceramics was tested.
Analysis of the effect of three sintering parameters (sintering temperature, sintering heating speed and sintering duration) on density of aluminum oxide ceramics was performed using response surface methodology, based on experimental data obtained according to Box-Behnken experimental design, using Design-Expert 11 program package.

• Ključne riječi: Al2O3 keramika; sinteriranje; metoda odzivne površine
• Ključne riječi (engleski): alumina; sintering; response surface method
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:235:809580
• Studijski program: Naziv: Strojarstvo; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka strojarstva (mag. ing. mech.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2019-05-22 23:42:30