Analiza toplinski obrađene Co-Cr dentalne legure izrađene 3D printanjem

završni rad

• Naslov (engleski): Analysis of heat-treated Co-Cr dental alloy made by 3D printing
• Autor: Fran Karačić
• Mentor: Zdravko Schauperl (mentor)
• Mentor: Dalibor Viderščak (komentor)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet strojarstva i brodogradnje; Zagreb
• Datum i država obrane: 2025-02, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Strojarstvo

Sažetak

U ovom radu se analizira utjecaj toplinske obrade na mikrostrukturu dentalnih Co-Cr legura izrađenih DMLS postupkom aditivne proizvodnje.
U teorijskom dijelu rada opisana je povijest Co-Cr legura, njihov sastav, svojstva, proizvodnja i primjena te utjecaj pojedinih elemenata u leguri. Na sličan način opisane su i dentalne Co-Cr legure. Opisan je postupak direktnog laserskog sinteriranja metala-DMLS te glavni parametri postupka. Objašnjen je i dijagramski prikazan proces toplinske obrade uzoraka nakon printanja, te je opisan način rada vakuumske peći i postupak žarenja.
U eksperimentalnom dijelu proveden je proces toplinske obrade dentalnih Co-Cr legura u vakuumskoj peći. Analizirana je mikrostruktura uzoraka u poliranom stanju pomoću svjetlosnog mikroskopa, provedeno je mjerenje tvrdoće uzoraka te određivanje udjela poroziteta u mikrostrukturi. Za kraj je napravljena analiza dobivenih rezultata i usporedba s rezultatima prije toplinske obrade te su rezultati grafički prikazani.

Sažetak (engleski)

This thesis analyzes the impact of heat treatment on the microstructure of dental Co-Cr alloys manufactured by using the DMLS additive manufacturing process.
The theoretical part of the thesis describes the history of Co-Cr alloys, their composition, properties, manufacturing process, and applications, as well as the influence of individual elements in the alloy. Similarly, dental Co-Cr alloys are also described. The direct metal laser sintering (DMLS) process and its key parameters are explained. Additionally, the heat treatment process of the samples after printing is described and illustrated, along with an explanation of the operation of the vacuum furnace and the annealing procedure.
In the experimental part of the thesis, the heat treatment process of dental Co-Cr alloys was conducted in a vacuum furnace. The microstructure of polished samples was analyzed using a light microscope, hardness measurements were performed, and the porosity percentage in the microstructure was determined. Finally, the obtained results were analyzed and compared with the results before heat treatment, and the findings were graphically presented.

• Ključne riječi: dentalne Co-Cr legure; toplinska obrada; mikrostruktura; tvrdoća
• Ključne riječi (engleski): dental Co-Cr alloys; heat treatment; microstructure; hardness
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:235:065505
• Studijski program: Naziv: Strojarstvo; Vrsta studija: sveučilišni; Stupanj studija: prijediplomski; Akademski / stručni naziv: sveučilišni/a prvostupnik/prvostupnica (baccalaureus/baccalaurea) inženjer/inženjerka strojarstva (univ. bacc. ing. mech.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2025-02-21 12:29:51