Analiza čvrstoće zida od aluminijske legure 6063 načinjenog aditivnom proizvodnjom električnim lukom i žicom

diplomski rad

• Naslov (engleski): Analysis of strength properties of 6063 aluminium alloy wall made by wire arc additive manufacturing
• Autor: Matej Čuček
• Mentor: Ivica Garašić (mentor)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Fakultet strojarstva i brodogradnje; Zagreb
• Datum i država obrane: 2024-12-05, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Strojarstvo; Proizvodno strojarstvo

Sažetak

Cilj ovog rada je analiza čvrstoće zida od aluminijske legure 6063 izrađenog aditivnom proizvodnjom električnim lukom i žicom, s posebnim naglaskom na vlačnu čvrstoću. U teorijskom dijelu opisani su postupci koji se koriste kod aditivne proizvodnje električnim lukom i žicom, s posebnim naglaskom na AC MIG i CMT postupak. Istražena je klasifikacija dodatnih materijala kod aditivne proizvodnje električnim lukom i žicom. Analizirana su mehanička i kemijska svojstva aluminijske legure 6063. U eksperimentalnom dijelu rada izrađeni su zidovi primjenom WAAM tehnologije. Iz ovih zidova oblikovane su epruvete namijenjene ispitivanju vlačne čvrstoće materijala. Također, izrađen je uzorak za statičko vlačno ispitivanje u skladu s normom HRN EN ISO 6892-1:2019.. Nakon provedenog statičkog vlačnog pokusa, dobiveni
rezultati uspoređeni su međusobno, kao i s mehaničkim svojstvima žice 6063 specificiranim od strane proizvođača. Pritom je analiziran utjecaj balansa polariteta AC MIG postupka na vlačnu čvrstoću, istezljivost i tvrdoću, s posebnim naglaskom na optimizaciju omjera pozitivnog i negativnog polariteta radi postizanja ravnoteže između toplinskog unosa i depozita materijala.
Također, u eksperimentalnom dijelu ispitivana je tvrdoća aluminijskog zida. Na osnovi dobivenih rezultata određeno je kod kojih se strojarskih komponenti može koristiti aditivna proizvodnja električnim lukom i žicom za aluminijsku leguru 6063.

Sažetak (engleski)

The aim of this study was to analyze the strength of a wall made from aluminum alloy 6063, produced using wire and arc additive manufacturing (WAAM), with a specific focus on tensile strength. The theoretical part describes the processes used in wire and arc additive
manufacturing, with a particular emphasis on the AC MIG and CMT processes. The classification of filler materials for wire and arc additive manufacturing was investigated. The mechanical and chemical properties of aluminum alloy 6063 were analyzed. In the experimental part, the preparation of samples for tensile testing was carried out in
accordance with HRN EN ISO 6892-1:2019. After conducting static tensile tests, the results were compared between samples and against the wire specification. Additionally, the hardness of the aluminum wall was tested in the experimental section. Based on the results, it is possible to determine which mechanical components can utilize wire and arc additive manufacturing for aluminum alloy 6063.

• Ključne riječi: Aluminijska legura 6063; aditivna proizvodnja; čvrstoća
• Ključne riječi (engleski): aluminum alloy 6063; additive manufacturing; strength
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:235:617922
• Studijski program: Naziv: Strojarstvo; smjerovi: Konstrukcijski smjer, Procesno-energetski smjer, Proizvodni smjer, Inženjersko modeliranje i računalne simulacije, Brodostrojarski smjer, Industrijsko inženjerstvo i menadžment, Inženjerstvo materijala, Mehanika i robotika, Autonomni sustavi i računalna inteligencija, Mehatronika i robotika; Smjer: Proizvodni smjer; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: sveučilišni/a magistar/magistra inženjer/inženjerka strojarstva (univ. mag. ing. mech.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Rad dostupan nakon; Datum isteka embarga: 2026-12-05
• Datum i vrijeme pohrane: 2024-12-02 11:58:41